Post-cure schedules for PRO-SET epoxy

Post-cure schedules vary depending on the resin/hardener combination, the desired laminate physical properties, and the capability of the  post-cure equipment to reach and maintain a target temperature.

During a post-cure, the temperature of the laminate is slowly raised to the post-cure target temperature, held for a period of time, then slowly lowered to room temperature.

Elevated temperature cure may begin as soon as the laminate is laid up, but with precautions. Keep in mind that as the uncured epoxy warms, it becomes more fluid and may drain from vertical laminates or result in a reduced resin-to-fibre ratio in some processes. In addition, in thicker laminations, the heat of the post- cure added to the exothermic heat generated by a large mass of curing epoxy may be high enough to damage the laminate or mould. For these reasons, post-cure should begin after the epoxy reaches an initial cure at room temperature.

The post-cure target temperature is usually determined by the mechanical or thermal properties desired, but may also be determined by limitations of the post-cure equipment, or the ability of core materials or the mould, to withstand post-cure temperatures.

Although minimum recommended post-cure temperatures may be lower, 60–82°C is the most effective range for post-curing PRO-SET® epoxies (other than when LAM-251-HT hardener is used). The target temperature determines the maximum potential properties a resin/hardener combination can reach. The highest gain in properties occurs within 8 hours, with diminishing gain up to 16 hours.

The laminate thickness will determine the rate of temperature increase. A thick laminate may require a hold cycle to allow the temperature to normalise throughout the laminate. A core can insulate a portion of the laminate, causing that portion to lag behind the average temperature rise. Use thermocouples to monitor the temperature at various locations on the component during post-cure.

Increase the laminate temperature at a controlled rate so the laminate temperature does not exceed the thermal properties of the epoxy in the laminate. As the laminate is heated, the epoxy will continue to cure. The temperature ramp rate should be slow enough to allow for this additional epoxy cure, pushing the thermal properties of the epoxy up ahead of the laminate temperature. If the laminate temperature exceeds the thermal properties of the epoxy, surface distortion or laminate print-through may occur.

Observe the following guidelines to avoid thermal shock during the post-cure cycles:

1. Increase the temperature from room temperature at a rate of 8–11°C per hour.

2. At every 22°C increase in temperature, hold that temperature for an extra hour to allow interior laminate temperatures to equalise. Resume the temperature increase of 8–11°C per hour.

3. Continue this cycle until the post cure target temperature is reached.

4. Hold the target temperature for a minimum of 8 hours (other than when LAM-251-HT hardener is used). The physical and thermal properties of the component will continue to improve until 100% of the potential properties are reached. Lower target temperatures require longer post cure times to reach 100%.

5. Decrease the temperature at a rate of 11°C per hour.

6. Hold at 35°C for two hours to allow for normalisation.

7. Turn off heat and allow to cool to room temperature. This schedule is recommended when curing a lighter laminate. The temperature ramp speed should be decreased for moulds, plugs and heavy laminates. We recommend building test panels of the finished laminate schedule to determine the ideal post-cure cycle. Thermocouple wires embedded in the test laminate will measure the temperature lag during the post-cure.

 

 

Subscribe to our newsletter so we can share with you our unique knowledge and experience of working with epoxy.

 

 

New Downloads

Latest PRO-SET news - Autumn 2017

Find out more
Post-curing is the controlled heating of an epoxy laminate—after it has reached or passed its initial cure stage—to improve the physical strength and thermal properties of the cured epoxy. Read an introduction to post-curing here.

Post-curing in moulds 
Generally, components are post-cured in the mould in which they were laminated. Click here to find out more about post-curing in moulds.

Our site uses cookies and similar technologies.

By clicking on the button below you agree to the cookies being used on this site. Learn more

I understand

Use of Cookies

Cookies provide information regarding the computer used by a visitor. We may use cookies where appropriate to gather information about your computer fin order to assist us in improving our website.

We may gather information about your general internet use by using the cookie.  Where used, these cookies are downloaded to your computer and stored on the computer’s hard drive. Such information will not identify you personally. It is statistical data. This statistical data does not identify any personal details whatsoever

You can adjust the settings on your computer to decline any cookies if you wish.  This can easily be done by activating the reject cookies setting on your computer.

Our advertisers may also use cookies, over which we have no control.  Such cookies (if used) would be downloaded once you click on advertisements on our website.

See our Privacy policy for more information

Bitnami